牌号简介 About |
---|
任务15是一种性能优异的聚氨酯树脂,在薄壁型铸件中表现出优异的冲击强度。任务15具有逐步固化的特点,使其非常适合旋转铸造应用。在室温下,使用寿命为6分钟,处理时间为60分钟。通过添加少量如此强烈的色彩或点燃荧光色彩,鲜艳的色彩是可能的。塑料完全固化,收缩率可忽略不计,可以进行机加工、打磨和/或喷漆。 TASK® 15 is a premium performance urethane resin that has very high impact strength, even when cast in thin-wall sections. Pot life is 6 minutes and handling time 60 minutes at room temperature. Resin cures with negligible shrinkage. Vibrant colors are possible by adding small amounts of SO-Strong® tint, UVO pigments or IGNITE® fluorescent colors. Plastic fully cures with negligible shrinkage and can be machined, sanded and/or painted. TASK® 15 features a gradual cure profile, making it ideal for rotational casting applications (making hollow parts). Applications include making very tough prototype parts and limited run production castings as well as rotationally cast parts such as mannequins. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.892 | cm³/g | ASTM D1475 |
收缩率 Shrinkage rate |
|||
MD MD |
0.42 | % | ASTM D2566 |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脱模时间 stripping time 2 |
|||
23℃ 23℃ 2 |
60 | min | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio |
75A:100B by weight | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
储存稳定性 storage stability |
|||
23℃ 23℃ |
min | ASTM D2471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cure Time |
【新闻资讯】查看全部
预防注塑尺寸不良,老技工有绝招
2018-06-01 尺寸偏小的不良 成形品偏小于规格尺寸 原因 地球上的东西大多数物质都有热胀冷缩的特性,树脂也一样,所以成形品被成形后开始收缩,一直冷却到与常温相等的时候,可是存在的问题是如果最后的收缩量过大的话,成形品尺寸变得过小,结果就造成了尺寸偏小不良,其原因之一是因为确定最初模具尺寸的时候,考虑到各种各样树脂的基本收缩率并将其数值计算出来作为参考,不过即使考虑了收缩率在实际进行当中也发 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |